Technical Specification
PRODUCT NAME : SCR-4700
Chemical Nature : Aqueous anionic dispersion of copolymer of acrylate. This product does not contain any plasticizers or solvents
Physical form : Milky White Liquid
Storage : Acrylic polymer SCR-4700 has a shelf life of 12 months. The air in the headspace of bulk storage tanks must be kept saturated with water vapor at all times
Application : Acrylic polymer SCR-4700 has the high binding force with other pigments in Cement application. It shows excellent Binding force and good water proof properties.
Technical Specification
|
|
|
Unit
|
Low limit
|
Upper limit
|
|
1
|
Non-volatile fraction(at150C/1hr)
|
%
|
46.0
|
48.0
|
|
2
|
pH(at 25C)
|
|
8.0
|
10.0
|
|
3
|
Viscosity(Rvt#2, 50rpm)
|
Cps
|
0
|
500
|
|
4
|
Specific Gravity(at 25C)
|
g/cm
|
1.01
|
1.05
|
|
5
|
Average Particle size
|
Nm
|
120
|
250
|
|
6
|
Ionic charge
|
|
Anionic
|
|
7
|
MFFT
|
C
|
17
|
Applications Examples
- Adhesive for cement and cement mortar, Tile adhesives.
- Polymer cement
- Reinforcing agent for cement concrete for high strength (Bridges and tunnels)
- Waterproof materials
Properties
- Excellent cement dispersion properties
- Excellent adhesion and compression strength
- Excellent water-proofing properties
- Excellent weathering and heat resistance
- Easy of Using (Good compatibility with defoamer, dispersant and other additives)
Formulation guide
- Plasticizer
Texanol, Butyl Carbitol, Butyl Cellosolve
- Filler
Calcium carbonate, Silica, Quartz, Dolomite
- Dispersing Agent
Nonionic polymeric dispersant, Sodium salt of polyphosphate
- Additives
Defoamers(NOPCO-NDW, NXZ), Levelling agent(BYK series)
Cautions
- Keep above 0 degreeC
- Sufficient mixing time is needed for adding plasticizers
- Adequate amount of defoamers is needed to prevent air foams which might bring about drop in compressing strength..
- Non-ionic surfactants(OP-40, NP-40) are helpful to reducing mixing viscosity of cement and binders, while for faster dispersing of cement polymeric type of non-ionic surfactants are preferred.
- Please contact to our research center when needed
------------------------------------------------------------------------------------------------------------
Technical Specification
PRODUCT NAME : SCA-8300
Chemical Nature : Aqueous anionic dispersion of copolymer of acrylate. This product does not contain any plasticizers or solvents
Physical form : Milky White Liquid
Storage : Acrylic polymer SCA-8300 has a shelf life of 12 months. The air in the headspace of bulk storage tanks must be kept saturated with water vapor at all times
Application
Acrylic polymer SCA-8300 has the high binding force with other pigments in Cement application. It shows excellent Binding force and good water proof properties.
Technical Specification
|
|
|
Unit
|
Low limit
|
Upper limit
|
|
1
|
Non-volatile fraction(at150C/1hr)
|
%
|
49.0
|
51.0
|
|
2
|
pH(at 25C)
|
|
8.0
|
10.0
|
|
3
|
Viscosity(Rvt#2, 50rpm)
|
Cps
|
0
|
500
|
|
4
|
Specific Gravity(at 25C)
|
g/cm
|
1.01
|
1.08
|
|
5
|
Average Particle size
|
Nm
|
120
|
250
|
|
6
|
Ionic charge
|
|
Anionic
|
|
7
|
MFFT
|
C
|
3
|
-------------------------------------------------------------------------------------------------------------
Technical Specification
PRODUCT NAM :SCE-5700
Chemical Nature : Aqueous anionic copolymer dispersion of acrylates. This product does not contain any plasticizers or solvents
Physical form : Milky White Liquid
Storage : Acrylic polymer SCE-5700 has a shelf life of 3 months. The air in the headspace of bulk storage tanks must be kept saturated with water vapor at all times
Application : Acrylic polymer SCE-5700 shows high tensile strength in the form of cement mixtures. It has the excellent water proof property and Good Elasticity.
Technical Specification
|
|
|
Unit
|
Low limit
|
Upper limit
|
|
1
|
Non-volatile fraction(at150C/1hr)
|
%
|
54.0
|
57.0
|
|
2
|
pH(at 25C)
|
|
7.0
|
9.0
|
|
3
|
Viscosity(Rvt#4, 50rpm)
|
Cps
|
200
|
2000
|
|
4
|
Specific Gravity(at 25C)
|
g/cm
|
1.02
|
1.08
|
|
5
|
Average Particle size
|
Nm
|
200
|
400
|
|
6
|
Ionic charge
|
|
Anionic
|
|
7
|
MFFT
|
C
|
- 10
|
-------------------------------------------------------------------------------------------------------------
Typical Physical Properties
Product name : SAV-5405 CM
Chemical Type : Polyvinyl acetate-co-acrylate
Polymer Type : Emulsion
Appearance : Milky-white liquid
Use : Interior Paint
|
Product name
|
SAV-5405 CM
|
|
Chemical Type
|
Polyvinyl acetate-co-acrylate
|
|
Polymer Type
|
Emulsion
|
|
Appearance
|
Milky-white liquid
|
|
Use
|
Interior Paint
|
|
Solid content
|
54.0%
|
|
pH
|
3.5-5.5
|
|
Specific gravity
|
1.06
|
|
Viscosity
|
Below 1000 cps
|
|
MFFT
|
5
|
|
|
|
SAV-5405CM is a copolymer of Vinyl acetate, acrylate, and Veova 10 for the LMC.
Applications Examples
- Adhesive for cement and cement mortar, Tile adhesives.
- Polymer cement- Reinforcing agent for cement concrete for high strength (Bridges and tunnels)
- Waterproof materials
Properties
- Excellent cement dispersion properties
- Excellent adhesion and compression strength
- Excellent water-proofing properties
- Excellent weathering and heat resistance
- Easy of Using (Good compatibility with defoamer, dispersant and other additives)
Formulation guide
- Plasticizer
TExanol, Butyl Carbitol, Butyl Cellosolve
- Filler
Calcium carbonate, Silica, Quartz, Dolomite
- Dispersing Agent
Nonionic polymeric dispersant, Sodium salt of polyphosphate Additives
Defoamers(NOPCO-NDW, NXZ), Levelling agent(BYK series)
Cautions
- Keep above 0 degree C
Sufficient mixing time is needed for adding plasticizers
-Adequate amount of defoamers is needed to prevent air foams which might bring about drop in compressing strength..
Non-ionic surfactants(OP-40, NP-40) are helpful to reducing mixing viscosity of cement and binders, while for faster dispersing of cement polymeric type of non-ionic surfactants are preferred.
Please contact to our research center when needed
--------------------------------------------------------------------------------------------------------------
Technical Specification
PRODUCT NAME : SCM-9000
Chemical Nature : Aqueous anionic dispersion of copolymer of styrene-acrylate. This product does not contain any plasticizers or solvents
Physical form :Milky White Liquid
Storage : Acrylic polymer SCM-9000 has a shelf life of 12 months. The air in the headspace of bulk storage tanks must be kept saturated with water vapor at all times
Application
Acrylic polymer SCM-9000 has the high binding force with other pigments in Cement application. It shows excellent Binding force and good water proof properties.
Technical Specification
|
|
|
Unit
|
Low limit
|
Upper limit
|
|
1
|
Non-volatile fraction(at150C/1hr)
|
%
|
46.0
|
48.0
|
|
2
|
pH(at 25C-
|
|
8.0
|
10.0
|
|
3
|
Viscosity(Rvt#2, 50rpm)
|
Cps
|
0
|
1000
|
|
4
|
Specific Gravity(at 25C)
|
g/cm
|
1.01
|
1.07
|
|
5
|
Average Particle size
|
Nm
|
120
|
250
|
|
6
|
Ionic charge
|
|
Anionic
|
|
7
|
MFFT
|
C
|
3
|
Applications Examples
- Adhesive for cement and cement mortar, Tile adhesives.
- Polymer cement
- Reinforcing agent for cement concrete for high strength (Bridges and tunnels)
- Waterproof materials
Properties
- Excellent cement dispersion properties
- Excellent adhesion and compression strength
- Excellent water-proofing properties
- Excellent weathering and heat resistance
- Easy of Using (Good compatibility with defoamer, dispersant and other additives)
Formulation guide
- Plasticizer
Texanol, Butyl Carbitol, Butyl Cellosolve
- Filler
Calcium carbonate, Silica, Quartz, Dolomite
- Dispersing Agent
Nonionic polymeric dispersant, Sodium salt of polyphosphate
- Additives
Defoamers (NOPCO-NDW, NXZ), Levelling agent (BYK series)
Cautions
- Keep above 0 degree C
- Sufficient mixing time is needed for adding plasticizers
- Adequate amount of defoamers is needed to prevent air foams which might bring about drop in compressing strength..
- Non-ionic surfactants(OP-40, NP-40) are helpful to reducing mixing viscosity of cement and binders, while for faster dispersing of cement polymeric type of non-ionic surfactants are preferred.
- Please contact to our research center when needed