Properties
|
SHP-40
|
SHP-60
|
SHP-100
|
|
Non-volatile fraction(at150°C/1hr)
|
36.5 - 38.5
|
28.5 - 30.5
|
26 - 27
|
|
pH(at 25°C)
|
9.0 - 10.5
|
9.0 - 10.0
|
9.0 - 10.0
|
|
Viscosity(Rvt#2, 50rpm)
|
0 - 500
|
0 - 500
|
0 - 500
|
|
Specific Gravity(at 25°C)
|
1.01 - 1.05
|
1.01 - 1.05
|
1.01 - 1.05
|
|
Average Particle size
|
450 - 650
|
600 - 850
|
900 - 1200
|
|
Ionic charge
|
Anionic
|
Anionic
|
Anionic
|
|
Hiding power(contrast ratio)*
|
0.70 - 0.85
|
0.70 - 0.85
|
0.70 - 0.85
|
SHP-60
Chemical nature : Aqueous anionic dispersion of copolymer of acrylic, styrene.
Physical form :
Milky White Liquid
Storage :
Acrylic polymer SHP-60 has a shelf life of 12 months. The air in the headspace of
bulk storage tanks must be kept saturated with water vapor at all times
Technical specification :
|
NO
|
SPECIFICATION
|
UNIT
|
LOW LIMIT
|
UPPER LIMIT
|
|
1
|
Non-volatile fraction(at150°C/1hr
|
%
|
28.5
|
30.5
|
|
2
|
pH(at 25°C)
|
|
9.0
|
10.0
|
|
3
|
Viscosity(Rvt#2, 50rpm)
|
Cps
|
0
|
500
|
|
4
|
Specific Gravity(at 25°C)
|
g/cm
|
1.01
|
1.05
|
|
5
|
Average Particle size
|
Nm
|
600
|
850
|
|
6
|
Ionic charge
|
-
|
ANIONIC
|
|
7
|
Hiding power(contrast ratio)*
|
°C
|
0.70~0.85
|
*Hiding power is evaluated from test of simple coating system
containing only Opaque polymer SHP-60 as a whitening pigment and Binder.
(SHP-60 : Binder =30 : 70 on Solid base, PWC = 30%)
Mixed composition is draw down 8mil bird Applicator on hiding power test paper.
----------------------------------------------------------------------------------------------------
SHP-40
Chemical nature : Aqueous anionic dispersion of copolymer of acrylic, styrene.
Physical form :
Milky White Liquid
Storage :
Acrylic polymer SHP-40 has a shelf life of 12 months. The air in the headspace of
bulk storage tanks must be kept saturated with water vapor at all times
Technical specification :
|
NO
|
SPECIFICATION
|
UNIT
|
LOW LIMIT
|
UPPER LIMIT
|
|
1
|
Non-volatile fraction(at150°C/1hr
|
%
|
36.5
|
38.5
|
|
2
|
pH(at 25°C)
|
|
9.0
|
10.5
|
|
3
|
Viscosity(Rvt#2, 50rpm)
|
Cps
|
0
|
500
|
|
4
|
Specific Gravity(at 25°C)
|
g/cm
|
1.01
|
1.05
|
|
5
|
Average Particle size
|
Nm
|
450
|
650
|
|
6
|
Ionic charge
|
-
|
ANIONIC
|
|
7
|
Hiding power(contrast ratio)*
|
°C
|
0.70~0.85
|
*Hiding power is evaluated from test of simple coating system
containing only Opaque polymer SHP-40 as a whitening pigment and Binder.
(SHP-40 : Binder =30 : 70 on Solid base, PWC = 30%)
Mixed composition is draw down 8mil bird Applicator on hiding power test paper.
-----------------------------------------------------------------------------------------------------
SHP-100
Chemical nature : Aqueous anionic dispersion of copolymer of acrylic, styrene.
Physical form :
Milky White Liquid
Storage :
Acrylic polymer SHP-100 has a shelf life of 4 months. The air in the headspace of
bulk storage tanks must be kept saturated with water vapor at all times
Technical specification :
|
NO
|
SPECIFICATION
|
UNIT
|
LOW LIMIT
|
UPPER LIMIT
|
|
1
|
Non-volatile fraction(at150°C/1hr
|
%
|
26.0
|
27.0
|
|
2
|
pH(at 25°C)
|
|
9.0
|
10.0
|
|
3
|
Viscosity(Rvt#2, 50rpm)
|
Cps
|
0
|
500
|
|
4
|
Specific Gravity(at 25°C)
|
g/cm
|
1.01
|
1.05
|
|
5
|
Average Particle size
|
Nm
|
900
|
1200
|
|
6
|
Ionic charge
|
-
|
ANIONIC
|
|
7
|
Hiding power(contrast ratio)*
|
°C
|
0.70~0.85
|
*Hiding power is evaluated from test of simple coating system
containing only Opaque polymer SHP-100 as a whitening pigment and Binder.
(SHP-100 : Binder =30 : 70 on Solid base, PWC = 30%)
Mixed composition is draw down 8mil bird Applicator on hiding power test paper.